At EGR Extrusion, we are continuously working on ways to improve environmental sustainability. Enhancing environmental performance through our ISO14001-2015 certification, we have set ourselves a goal to turn waste into wonders.

Key Advantages:

Sustainable Marvel: EcoSheet is a testament to our commitment to the environment. Crafted from reclaimed Acrylic ABS waste, it's a sustainable solution that reduces ecological impact. Available in 2mm to 8mm gauge in a smooth or textured finished, EcoSheet suits your ABS fabrication and thermoforming needs.

Uncompromised Strength:

Boasting a tensile strength of 63 MPa, EcoSheet is engineered to excel. Its strength and resilience ensure durability in diverse applications.

Versatility Redefined:

From its Vicat softening temperature of 99°C to a continuous service temperature of 75°C, ECOSHEET adapts seamlessly to your needs.

Fire-Resistant Guardian:

With a self-ignition temperature of 430°C and a glow wire ignition temperature of 725°C, ECOSHEET offers superior fire resistance.

Density: 1.09 g/cm³ (ISO 1183-1:2019 Method A)

Water Absorbtion: 0.95% (ISO 62:2008)

Mechanical Excellence:

Tensile Strength: 41MPa (ISO 527-2:2012)

Tensile Strain at Break: 40% (ISO 527-2:2012)

Tensile Modulus: 2300 MPa (ISO 527-2:2012)

Flexural Strength: 68 MPa (ISO 178:2019 Method A,B)

Flexural Modulus: 2530 MPa (ISO 178:2019 Method A,B)

Izod Impact Strength, Notched: >177.96 kJ/m² (ISO 180:2000+Amd.2:2013)

Thermal Performance:

Vicat Softening Temperature:: > 99°C (ISO 306:2013)

Heat Deflection Temperature, 1.82MPa:: > 88°C (ISO 75-2:2013)

Coefficient of Linear Thermal Expansion:: 8.4 m/m·K x 10-5 (DIN53752)

Self Ignition Temperature:: 450°C (ASTM D 1929)

Flash Ignition Temperature:: 370 °C (ASTM D 1929)

Join the ECOSHEET Revolution

Contact us today to explore how EcoSheet can infuse sustainability, strength, and style into your next project. Let's co-create a future that's both visionary and eco-friendly.